SOOT combustion. co and k catalysts supported on different supports

The catalytic combustion of particulate material was studied on cobalt catalysts promoted with potassium using different supports for its preparation. Silica, aluminium oxides and hydroxides, zirconium oxide and hydroxide were used as supports. The catalytic activity for combustion depends on the type of support used, the higher activity corresponding to the supported catalyst on zirconium oxide. TPR studies indicate that the interaction metal/support allows to explain the higher activity of the CoK/SiO₂ catalyst with respect to the CoK/Al₂O₃ but the high activity found in CoK/ZrO₂is not explained by this interaction. In all cases the Co and K improved the performance of the catalysts.     

Y2O3涂层负载Pd整体式催化剂的制备和催化性能

以Y(NO3)3为前驱体制备了Y2O3涂层的堇青石蜂窝陶瓷载体.扫描电子显微镜、X射线能谱和超声波振荡等表征结果表明,Y2O3涂层不但具有良好的抗振荡性和粘结强度,而且具有很强的吸附催化剂活性组分(H2PdCl4)的能力,适合制备负载型Pd催化剂.以甲苯和乙酸乙酯完全燃烧为模型反应考察了催化剂的活性,发现以Y2O3涂层堇青石蜂窝陶瓷为载体的整体式Pd/Y2O3催化剂具有良好的催化活性和热稳定性,甲苯和乙酸乙酯催化燃烧的T99分别为210和300℃;催化剂经900℃焙烧4 h后,T99仅提高20℃,表明催化剂具有很高的热稳定性.催化剂的X射线衍射、拉曼光谱和程序升温还原结果表明,Pd/Y2O3催化剂经低温焙烧时,Y2O3和PdO均高度分散在堇青石蜂窝陶瓷的表面,而高温焙烧使催化剂活性组分PdO晶粒增大,从而导致催化剂活性下降.     

PREPARATION OF CUO/γ-Al2O3 CATALYSTS FOR CATALYTIC COMBUSTION VOCS VIA PLASMA

CuO/γ-Al2O3 catalysts were prepared by plasma treatment and conventional impregnation methods. The catalytic combustion of two kinds of volatile organic compounds (VOCs), toluene and benzene, were carried out over these CuO/γ-Al2O3 catalysts. The surface properties of these catalysts were characterized by X-ray Diffraction (XRD) and Scanning Electron Microscopy (SEM). The experimental results showed that in catalytic combustion the activity of the CuO/γ-Al2O3 catalyst prepared via plasma was much higher than that of the CuO/γ-Al2O3 catalyst prepared by conventional impregnation method. XRD results showed that an enhanced dispersion had been achieved with the plasma treatment. SEM results indicated that the size became much smaller and the surface became more uniform with the plasma treatment.     

K-Ce_(0.5)Zr_(0.5)O_2催化碳颗粒物燃烧性能

用等体积浸渍法制备了不同K负载量的xKNO3-Ce0.5Zr0.5O2系列催化剂,用程序升温氧化反应(TPO)考察催化剂对碳颗粒物(soot)燃烧的催化活性.并采用XRD、BET、FT-IR、XPS等技术对KNO3负载催化剂进行表征.结果表明KNO3负载量对催化剂的比表面、表面化学环境有显著的影响;KNO3能使催化剂对soot的催化燃烧活性有较大提高,且存在最佳负载量,当x=0.5时,催化剂的活性最好,碳颗粒物的起燃温度(T)i和峰顶温度(Tp)分别为290℃和360℃.在反应过程中,KNO3熔融状态的形成和K2CO3的生成,使催化活性明显提高.     

Effect of Drying Methods on the Structure and Combustion Activity of Mn—Substituted Hexaaluminate Catalysts

Conventional oven drying (COD) and supercritical drying (SCD) methods were applied to the preparation of Mn-substituted hexaaluminate (BaMnA111O19-α) catalysts. The effect of drying methods on phase composition, specific surface area, pore structure, reduction behavior of Mn^3 ions, and combus-tion activity of the samples was investigated. The homogenous mixing of the components in the sol-gel process could be maintained by SCD, and the hexaaluminate phase was almost the only phase of the resulting materials after calcination. H2-TPR revealed that the Mn^3 ions in the sample obtained by SCD were easier to be reduced than that by COD. Moreover, the samples obtained by SCD have higher surface area, narrower pore size distribution, and higher combustion activity than those obtained by COD.     

Kinetics of catalytic combustion in air over Pt/Al2O3/Al catalyst

Summary Catalytic combustion of toluene, propylene and CO over Pt/Al₂O₃ /Al catalyst was investigated. Strong inhibition effects are observed when the mixture of toluene, propylene and CO is oxidized. A reaction mechanism of catalytic combustion over Pt/Al₂O/Al is proposed. The results from kinetic models are in good agreement with the experimental data.     

Gd_3Al_5O_(12)∶Eu~(3+)柠檬酸盐硝酸盐燃烧法合成及其发光性能研究

采用柠檬酸盐硝酸盐燃烧法,在较低的温度(900℃)下成功地合成单一晶相Gd3Al5O12∶Eu3+发光粉体,紫外激发荧光光谱分析表明,粉体615 nm和593 nm荧光发射源于Eu3+的5D0-7F2和5D0-7F1跃迁.该方法中各工艺条件(如pH值、柠檬酸/金属离子比、煅烧温度)对Gd3Al5O12∶Eu3+发光性能均有影响,通过试验得出了获得最佳发光性能荧光粉体的工艺参数.     

轻工业纤维素生物质过程残渣能源化技术

以农产品为原料的轻工业大都是典型的流程工业,在通过转化过程将原料转化为食品、饮料、添加剂、调味料、纸和中成药等产品的同时产生被称为过程残渣的固体废物与废料,如白酒糟、酒精糟、醋糟、甘蔗渣、中药渣、油粕、酱渣、菌渣和造纸黑液可熔渣等.这些残渣产生于特定的生产过程,富含纤维素、蛋白质或木质素,因此代表一种已经被集中的生物质资源.它们同时含水50%-80%、易腐烂变质、甚至呈弱酸碱性,因此是重要的环境污染源.本文着眼于轻工生物质过程残渣的高值化利用,分析指出富含纤维素的白酒糟、醋糟、甘蔗渣、中药渣、茶渣和造纸边角料等适合作为生物质能源而被转化利用,并根据资源特征提出了可能的技术路线.通过分别对热化学路线涉及的脱水干燥、燃烧发电与气化发电技术和集成乙醇发酵、沼气发酵的复合转化技术进行技术综述,最后针对不同规模的富含纤维素轻工生物质过程残渣能源化提供了技术选择建议.     

MCM-41负载的La, Ce和Pt催化剂上三氯乙烯的低温催化燃烧

 分别采用直接水热合成法和浸渍法制备了Si-MCM-41, La-Si-MCM-41和Ce-Si-MCM-41介孔材料及其负载的Pt催化剂. 小角X射线衍射、氮气吸附和扩展X射线精细结构分析表明, La和Ce元素进入了MCM-41分子筛的骨架结构. NH3程序升温脱附测试未检测到含La和Ce样品表面的酸性. 所制备的催化剂具有较高的三氯乙烯催化燃烧活性及生成CO2和HCl的选择性.     

Methane Combustion Over Fe, Co and Ni Modified Manganese Oxide Catalysts

Fe-Mn, Co-Mn and Ni-Mn composite oxide catalysts based on high specific surface area MnO₂ precursor were prepared and applied to catalytic combustion of CH₄. Results were compared with that of unmodified MnOx and 1wt.% Pd/-Al₂O₃. Below 450°C, manganese oxide catalysts show higher activity than Pd/-Al₂O₃, while the modified manganese oxide catalysts exhibit higher activity than the unmodified one below 420°C. All catalysts were characterized by means of N₂-BET, XRD, TG-DTA and H₂-TPR. Due to the interaction between Fe, Co or Ni oxides and manganese oxide, the activity of the oxygen species of the modified catalysts is improved, which leads to the increase of their CH₄ combustion activity.